249 | 1.09 | 260 | .93 |
| | 2 by 10 | 180 | 5 | 13.8 | 24.8 | 3,757 | .79 | 4,606 | .59 | 1,198 | 1.05 | 186 | .67 |
| | 2 by 8 | 180 | 6 | 13.7 | 20.7 | 4,314 | .90 | 5,050 | .65 | 1,313 | 1.15 | 166 | .60 |
| | 2 by 2 | 28 | 122 | 15.2 | 18.8 | 4,777 | 1.00 | 7,798 | 1.00 | 1,146 | 1.00 | 279 | 1.00 |
| Norway pine | 6 by 12 | 162 | 5 | 16.7 | 8.1 | 2,968 | .56 | 5,204 | .61 | 1,123 | .97 | 286 | 1.02 |
| | 4 by 10 | 162 | 5 | 13.7 | 12.0 | 5,170 | .98 | 6,904 | .82 | 1,712 | 1.48 | 317 | 1.13 |
| | 2 by 2 | 30 | 60 | 14.9 | 11.2 | 5,280 | 1.00 | 8,470 | 1.00 | 1,158 | 1.00 | 281 | 1.00 |
|-----------------------------------------------------------------------------------------------------------------------------------|
| _Note.--Following is an explanation of the abbreviations used in the foregoing tables:_ |
| F.S. at E.L. = Fiber stress at elastic limit. |
| M. of E. = Modulus of elasticity. |
| M. of R. = Modulus of rupture. |
| Cr. str. at E.L. = Crushing strength at elastic limit. |
| Cr. str. at max. ld. = Crushing strength at maximum load. |
|-----------------------------------------------------------------------------------------------------------------------------------|

|-----------------------------------------------------------------------------------------------------------------------------------------------|
| TABLE XXI TABLE XXI |
|-----------------------------------------------------------------------------------------------------------------------------------------------|
| COMPRESSION AND SHEAR TESTS ON AIR-SEASONED MATERIAL